The Elephant Has Left the Room – 450 mm is a Go!

It's the day before Semicon opens up, and we have had a slew of announcements on 450 mm, the biggest of which was the joint ASML/Intel notice that Intel will be taking a share of ASML as a way of funding 450 mm and EUV R&D. Simultaneously imec released that the Flemish government would invest in their upcoming 450-mm facility, and imec and KLA-Tencor declared that a 450-mm capable SP3 450 unpatterned wafer defect inspection tool had been installed at imec.

ASML announced it as a “co-investment program” in which Intel would invest EUR829 million (about $1B) over the next five years, EUR553M of which would be in 450 mm R and D. Intel focused more on the R and D and described the financial details later.

They cited the classic economics of doubling the wafer size, and the potential die cost reduction:

All of which is logical, but ASML has been notably reticent about making any comments on 450-mm R and D in the past, to the point where some industry watchers (including me) have wondered if we would ever get there; if the biggest litho vendor isn’t on board, there won't be any 450-mm fabs even if all the other equipment companies are ready.

Which brings me to the elephant in the title. Last year at Semicon there was a 450 mm panel, and everyone was pontificating wisely, until Bob Johnson of Gartner commented on "the elephant in the room - ASML has no 450-mm program, so why are we bothering to even talk about it?" (my paraphrasing). Which kind of shut the whole thing down.

However, that particular pachyderm has clearly moved on, and we have an ASML roadmap with both 450 mm and EUV in it:

We won’t have any production tools until 2018, but at least a huge barrier to adoption is lifted; now there are just the simple engineering tasks of getting a substrate the size of a turkey platter exposed with patterns with feature sizes of 14nm or smaller. Has anyone said that this industry is crazy?

By coincidence Mike Splinter of Applied Materials was speaking at the imec Technology Forum, and he commented that 300-mm had just about paid off its development costs as of now, roughly 14 years after the launch of the first systems. He guesstimated the costs for developing 450 mm as $15 - 20B, with an as yet unknown payoff time. (Has anyone said that this industry is crazy?) However,  he also said this time last year that Applied would spend over $100M on 450 mm and that "450 mm is going to happen."

Clearly Intel has recognised that if it wants 450 mm to go forward, then it has to pony up some cash to encourage the litho side, and it is already invested in the consortium being set up at Albany. For anyone interested in the financial side of the deal, check out the press releases linked above, or watch ASML CFO Peter Wennink in a video.

Looks like 450 mm is actually going to happen!

Sony’s PS Vita Uses Chip-on-Chip SiP – 3D, but not 3D

At the tail end of last year Sony released their PlayStation Vita, and it was duly torn down by iFixit and others. In due course we took it apart too, though we didn’t post it on our teardown blog.

Sony CXD5315GG in the PlaySation Vita

Inside we found the usual set of wireless chips, motion sensors, and memory, but the key to the increased performance of the PS Vita is the Sony CXD5315GG processor, a quad-core ARM Cortex-A9 device with an embedded Imagination SGX543MP4+ quad-core GPU.

Above I said that we found memory, but actually the only discrete memory that we found on the motherboard was 4 GB of Toshiba flash; and Sony’s specification states that there is 512 MB (4 Gb) regular RAM, plus 128 MB (1 Gb) VRAM (video RAM). In a phone that would tell me that there is memory in a package-on-package (PoP) configuration, mobile SDRAM in the top part and the processor in the bottom part.

However, when we took the part off the board and did a set of x-rays, the side view proved me wrong – it’s a stack, and the close-up shows that there appear to be five dies in there, a thick die at the base, a thinner one immediately on top and three smaller die on top of that. The second die down could be a spacer, since there don’t seem to bond wires going to it.

Side x-ray images of Sony CXD5315GG

This immediately led us to speculate – if the second die up is the VRAM, is it wide I/O DRAM, and is it using through-silicon vias (TSVs)? Time for a real cross-section to check that out, and almost predictably we were disappointed:

Sony CXD5315GG package cross-sectioned

This type of face-to-face connection showed up back in 2006 in the original Sony PSP, and Toshiba had dubbed it “semi-embedded DRAM”, now they are calling it “Stacked Chip SoC”. The ball pitch is an impressive ~45 µm, almost as tight as TI’s copper pillars, but they are staggered to achieve 40-µm pitch.

So what are the five chips that are in the stack? At the base we have the processor chip; face to face with it is a Samsung 1-Gb wide I/O SDRAM; and the top three dies comprise two Samsung 2-Gb mobile DDR2 SDRAMs, separated by a spacer die, and conventionally wire-bonded. The base die is ~250 µm thick, and the others ~100 – 120 µm.

When we look at the die photos of the processor and the 1-Gb memory, we can see that they are purposely laid out for the stacked-chip configuration, since in the centres of both is an array of matching bond pads.

Die photos of the Sony CXD5315GG (left) and Samsung 1-Gb wide I/O SDRAM with bond pad arrays annotated

Close examination reveals that there are 1080 pads in two blocks of 540 (2 sub-blocks of 45 rows of 6 pads), so likely 2 x 512 bit I/O operation, possibly sub-divided into 4 x 128.

Wide I/O bond pad arrays in Sony CXD5315GG (top) and Samsung SDRAM

Last year at ISSCC Samsung described a similar wide I/O DRAM using TSVs [1], claiming a data bandwidth of 12.8 Gb/s, four times the bandwidth of an equivalent LPDDR2 part. I doubt that the authors expected their design to be in a volume consumer device before the end of the year, but that seems to be what happened!

Chip architecture of Samsung 1Gb Wide-I/O DRAM and SEM image of microbumps (Source: Samsung/ISSCC)

This uses similar I/Os, but not the same as, the JEDEC wide I/O standard issued earlier this year (which calls for 50 rows of 6 pads in each block), and of course it predates it by about a year.

By combining the processor with the different memories in the same package in the Vita, Sony and Toshiba have produced one of the few true system-in-package (SiP) parts that we have seen. And I would call it 3D, even though industry convention is now restricting that term to TSV-based parts – so it’s not 3D, in our current argot.

In a way this device highlights the commercial barriers to introducing TSVs into the SiP world, since not only do the corresponding parts have to be designed to suit the I/Os, but at least for a two-stack the technology is already there; so the performance cost/benefit has to be critical enough to require TSVs for that third and more die. Admittedly the demands on mobile devices are increasing at an astounding pace, but it still seems a while before we’ll see TSVs in commercial devices. Time will tell!

[1] J-S. Kim et al., A 1.2V 12.8GB/s 2Gb Mobile Wide-I/O DRAM with 4×128 I/Os Using TSV-Based Stacking, ISSCC 2011, pp. 496 – 498.

Intel’s 22-nm Trigate Transistors Exposed

Last week Intel had their Q1 conference call for financial analysts, and revealed that the 22-nm Ivy Bridge parts would make up 25% of their shipment volume in the second quarter of this year.  That means that a good quantity will already will have shipped, and we managed to track some down in Hong Kong a few weeks ago.  Of course we got in touch ASAP and the parts duly arrived, and they were the real thing.

Fig. 1 Intel Xeon E3-1230V2 Server CPU

We obtained samples of Xeon E3-1230 v2 CPUs, which are four-core, 3.3 GHz, 64-bit parts intended for the server market. Here is a die photo of the transistor level, with annotations from Intel's Ivy Bridge launch yesterday:

Fig.2 Intel Xeon E3-1230V2 Die

A quick cross-section reveals that Intel have stayed with the nine metal layers used in the last two generations:

Fig. 3 Intel Xeon E3-130V2 General Structure

A closer TEM image (Fig. 4) shows the lower metal stack and a pair of multi-fin NMOS and PMOS transistors. This section is parallel to the gate, across the fins, and we can see the contact trenches and metal levels M1 up to M5.

We have to digress here a little to explain what we’re looking at.  A typical TEM sample is 80 – 100 nm thick, to be thin enough to be transparent to the electron beam and at the same time have enough physical rigidity so that it does not bend or fall apart.

Here we are trying to image structures in a die with a gate length of less than 30 nm; so if we make a sample parallel to the gate, and if the sample is aligned perfectly along the centre of the gate, then it will contain the gate plus at least part of the source/drain (S/D) silicon and contacts on either side.

Fig. 4 TEM Image of Lower Metals and NMOS and PMOS (right) Transistors

That is what we see above – I have labeled the gate and contact stripes, and we have PMOS on the right and NMOS on the left.  The tungsten-filled contacts obscure parts of the gate, but we can clearly see that the PMOS S/D fins have epitaxial growth on them, and the fins have an unexpected slope – a little different from Intel’s tri-gate schematic shown last year –see Fig.5.

Fig. 5 Intel Schematic of Tri-Gate Transistor

If we zoom in a bit further into the PMOS gate (Fig. 6), we can see how the gate wraps over the fin, and the rounded top of the fin.  The thin dark line adjacent to the fin is the high-k layer and just above that is a mottled TiN layer that is likely the PMOS work-function material, as in the 32-nm and 45-nm parts.

Fig. 6 TEM Image of PMOS Gate and Fin Structure

Fig. 7 shows a section of an NMOS transistor.  There is a ‘ghost’ of the contact behind the gate, but the gate structure itself looks similar to the PMOS, with the exception of the work-function material just above the high-k layer (as expected).

Fig. 7 TEM Image of NMOS Gate and Fin Structure

Fig. 8 gives me an opportunity to show off our new TEM – we have recently purchased an FEI Osiris machine, which upgrades our capability considerably. Here we have a lattice image of a fin in an NMOS transistor; the diamond-like layout of the pattern of dots is actually created by the columns of atoms in the silicon crystal lattice. This tells us that the sample is oriented in the <110> direction, which given that silicon has a face-centred cubic structure in which equivalent planes are at right angles, means that the channel direction is also <110>.

Fig. 8 TEM Lattice Image of NMOS Fin Structure

To fully understand what we’re looking at, of course, we need to see what’s happening in the orthogonal direction, along the fin and cross-sectioning the gate – as in Fig. 9. This shows an array of PMOS transistors over a single fin, four functional gates and two dummy gates at the ends of the fin. Again the TEM sample is thick compared with the feature size, so we are seeing the gate on the side(s) of the fin, not just the top. The fin ends have the same taper as in Figs 6 and 7.

Fig. 9 TEM Image of PMOS Transistors

As announced by Intel, there is embedded SiGe in the source/drains, although not etched to the <111> planes as in the 32- and 45-nm product. It also looks as though the tops of the gates have been etched back and back-filled with dielectric, and the contacts are self-aligned as in memory chips.

Zooming in on the PMOS transistor in Fig.10, the image is a bit fuzzy, but the SiGe is clearly in a rounded cavity with no facets on the top, though there are facets on the sides of the fin (see fig. 4).

Fig. 10 TEM Image of PMOS Transistor

Looking at the NMOS equivalent (Figs. 11 and 12), we see a similar structure – there seems to be an epitaxial interface, and the silicide(?) seems to protrude slightly above the fin.

Fig. 11 TEM Image of NMOS Transistors

Fig. 12 TEM Image of NMOS Transistors

 It is hard to say much about the gates here, either NMOS or PMOS, because of the sample thickness problem; we are viewing a slice that includes the gate on both sides of the fin and the fin itself. Fortunately we have images of gate metal over STI and they are less confusing. 

Figure 13 is a composite image of NMOS and PMOS gates so that the differences are highlighted. The dark line surrounding the gate structures is the Hf-based high-k, and within that are the two work-function materials, likely TiN for PMOS and TiAlN for NMOS. (The columnar structure of the PMOS TiN is visible in the right half of the image.)

Fig. 13 Composite TEM Image of NMOS/PMOS Gates

The fill has been changed from TiAl in the earlier parts to tungsten. It is more prominent in the NMOS gates than the PMOS, because the PMOS structure includes both work-function metals, whereas the TiN has been etched out of the NMOS gates. At the 45-nm node Intel used tensile tungsten in the contacts to apply channel stress – have they transposed this to the gates in the 22-nm process?

Just to finish up, so that this is still a blog, not a paper (I don’t want to go on too long) – fig. 14 shows a sample delayered to expose the transistors, and imaged on a tilt angle.  Both the gates and the fins show up nicely, and we can actually see tiny spikes of SiGe in the PMOS source/drains. The small pillars in between the fins in the NMOS areas are residual bits of contact metal.  I think it’s a cool image!

Fig. 14 Tilt SEM Image of NMOS/PMOS Transistors

We are just getting into the full scope of the analysis, so likely more to come in the next few weeks!
I'm still tweeting as @ChipworksDick, for those that way inclined..

Intel to Present on 22-nm Tri-gate Technology at VLSI Symposium

Just published is the press release and tip-sheet on the 2012 VLSI Symposia on VLSI Technology and Circuits, this year in Hawaii. Listed first in the VLSI Technology highlight papers is Intel’s paper, “A 22nm High-Performance and Low-Power CMOS Technology Featuring Fully Depleted Tri-Gate Transistors, Self-Aligned Contacts and High-Density MIM Capacitors”, to be presented by Chris Auth in slot T15-2.

There was a fair bit of frustration at last year’s IEDM that there was no Intel paper on their tri-gate technology, although they had several others at the conference. The Intel folks I talked to said that there was reluctance to publish, since the other leading-edge semiconductor companies were not presenting – conferences were no longer the exchange of information that they have been in the past. I have to say I agree, some companies are keeping their technological cards very close to their corporate chests these days!

Also, no product was in the public domain at that point, though Intel claimed to be in production. By the time VLSI comes around in June, we should all be able to get Ivy Bridge based Ultrabooks, and we at Chipworks will have pulled a few chips apart.

In the paper the process is claimed to have “feature sizes as small as eight nm, third-generation high-k/metal gate stack technology, and the latest strained-silicon techniques. It achieves the highest drive currents yet reported for NMOS and PMOS devices in volume manufacturing for given off-currents and voltage. To demonstrate the technology’s versatility and performance, Intel researchers used it to build a 380-Mb SRAM memory using three different cell designs: a high-density 0.092- µm2 cell, a low-voltage 0.108- µm2 cell, and a high-performance 0.130-µm2 cell. The SRAM operated at 4.6 GHz at 1 V.”

The tip-sheet also posted the first Intel tri-gate images that I’ve seen in a while:

TEM images of Intel 22-nm PMOS tri-gate transistor (a) and source/drain region (b)

Here we are looking at sections parallel to the gate, across the fin. There is no scale bar, so fin width is an unknown; and the taper on the fin is a bit of a surprise. The top of the fin is rounded, likely to avoid reliability problems from electric field concentration at corners.

In the gate metal, there seems to be a layer of titanium nitride (TiN) above the thin dark line that is the high-k, so we can surmise that the PMOS work-function metal is TiN, as in previous generations. The gate fill itself is very black, so that appears to have been changed from the Al/Ti fill used before; possibly to tungsten or some other heavier metal.

The source/drain image confirms the use of epi, and the darker area is again likely SiGe, both for strain and resistance improvement. At the moment it’s hard to say if the taper is a function of manufacturing convenience (easier to etch?), or if there are some device physics advantages that improve transistor operation. We’ll see in June!

Dialog Semi Gets the Girls for Apple

Over the years we have looked at a number of products from Apple, and in their mobile products we have seen a continuous series of design wins for power management chips from Dialog Semiconductor, all custom-made parts since they have not been in their normal product listings. 

One of the distinguishing features of each part has been the code names Dialog has used for them - as my colleague Jim Morrison has noted, they are all girl's names starting with A! Now read on..

Contributed by Jim Morrison

When it comes to Apple, the letter “A” features very prominently at Dialog Semiconductor.

Why, you ask? Every time we take a look at the power management ICs in Apple products, we find another Dialog Semiconductor device that has been named with a female first name, beginning with “A,” as we previously blogged about with Dialog Semiconductor's design win in the iPad 2.

Our most recent examination of the iPad 3 revealed Amelia in the PMIC for Apple's newest tablet.


Amelia (D1974A) from the New iPad

Does Dialog like to code their products so that all devices developed for Apple begin with A? Does renowned secrecy at Apple require all suppliers to be so hush-hush that to avoid errors, they talk about Apple using code names? Or does the power management team at Dialog just have a thing for female first names beginning with "A"? Perhaps the design manager has a family of daughters that all have names beginning with A. My family is all names with J so it’s quite possible another family has all As.

The iPhone 3 and 3GS liked Amanda, the iPhone 4 and the iPad 1 liked Ashley (Dialog Semiconductor D1815A), the iPhone 4s has Angelina, Dialog Semiconductor D1881A (my favourite), the iPad 2 has Alison (Dialog Semiconductor D1946A), and now our iPad 3 has chosen Amelia.

Amanda (D1755A) from the iPhone 3 and 3GS



Ashley (D1815A) from the iPhone 4 and the iPad 1



Angelina (D1881A) from the iPhone 4S



Alison (D1946A) from the iPad 2

 These die markings are changing because the die design has changed to accommodate new power requirements as we went from A4 processors to A5 to A5X, and other modifications in products that required changes to the PMIC.

We will see if the series continues in the iPhone 5 expected in the next few months..

Semicon China – SMIC Shows off 28-nm HKMG Development

Another foundry goes gate-last

In the opening keynote at Semicon China today, Dr. Tzu-Yin Chiu, CEO of SMIC, gave a run-through of their technology portfolio, and in doing so let out a few details of their sub-40 nm process development.

SMIC's Process/Application Portfolio

It appears that they are actually shipping some 40-nm pilot product for revenue, and to keep the ARM-world happy, they will have Cortex A9 cores running at 1.2 GHz by the end of the year.

Snapshot of advanced nodes at SMIC

Scheduled for mid-2013, their 28-nm offering will be both high-k, metal gate and poly/SiON, and feature one of the smallest SRAM cell sizes to date.

SMIC's 28-nm schedule

The images are all distinctly fuzzy thanks to the challenges of using a phone camera at some distance from a dimly-lit screen, but they show what I’m talking about. It appears that the gate-last structure has more in common with TSMC’s 28-nm structure than Intel’s 32-nm, and also that the NMOS and PMOS labels have been reversed.

SMIC 28-nm transistors and SRAM cell

In all the other gate-last HKMG transistors we have seen, the thick TiN and Ta layers are in the PMOS (you have to squint to distinguish them in this image, but they are there), and I wouldn’t expect SMIC’s to be any different. We can also see the tell-tale notch at the base of the transistors that indicates that the gate dielectrics were formed before the dummy poly gate was put down.  At less than 0.13 sq. microns the SRAM cell is the smallest that I know of – TSMC is 0.15, and Intel 0.17 sq. microns.

Just for comparison, here’s a pair of composite images of Intel’s 45-nm transistors and TSMC’s 28-nm transistors. You can clearly see the notches at the bottom of the gate structures that I refer to above.

Intel 45-nm transistors (left) and TSMC 28HPL transistors

The inclusion of a poly/SiON variant (presumably low-power) at 28 nm puts them on a par with TSMC and UMC, and leaves GLOBALFOUNDRIES as the only major foundry without an announced non-HKMG LP process at that node. If the rumours about GloFo second-sourcing the Qualcomm S4 (currently on TSMC’s poly/SiON 28LP line) are true, presumably they’ll have to develop one!

GloFo’s FinFETS are Better than Intel's! Musings from CPTF

This confident statement came from Subramani (Subi) Kengeri of GLOBALFOUNDRIES (GloFo) during the panel session in the GloFo/IBM/Samsung Common Platform Technology Forum (CPTF), held Wednesday in the Santa Clara Convention Center. I’m currently on one of my periodic road trips, and this one has given me the chance to sit in on the CPTF – last year I had to make do with the online version.

Towards the end of the panel discussions, the host, Jaga Jagannathan of IBM, asked Subi “How do you stack up against Intel? – especially in the SoC/smartphone space?” This clearly took Subi by surprise, but after some preamble, he focused on FinFET development, which AMD, then GloFo, have been working on for the last ten years.  In conjunction with customer input, they have been focusing their finFET efforts to optimise the (14 nm) process for mobile SoCs. He said that this was what would differentiate them from Intel, and in that space “We believe we have a much better finFET, that is optimised for mobile SoCs”.

CPTF panel session. Jaga is on the left, and Subi third from the right.  Source: Common Platform

Of course time will tell, and the CPTF 14-nm process will likely not show up for three or four years, while we are waiting for Intel’s imminent launch of their trigate product.

The panel session has been put online, so you can see it by going here, register if you need to, then select Agenda and click the relevant link; if you want to see this particular Q & A, move the slider to the 52:30 timepoint.

Also during the discussion Subi stated that GlobalFoundries is in production for 32-nm HKMG, and running the full flow of the 20-nm (gate-last) process in their Malta NY fab.

Earlier in the day he had given one of the keynote talks, and it was then that he gave the logic for the move to finFET at 14-nm that was a major theme of the day.  It boils down to the fact that by the time you get to the 20-nm node, there are no more knobs to turn to crank up the performance of a transistor.  In order to mitigate the short-channel effects and increase drive current, a 3D fully-depleted structure is needed. GloFo regards the mobile sector as one of the big drivers for leading-edge process development these days, so their finFET efforts have been focused in the mobile SoC arena, with a multiple Vt process in development.

Another nugget from the day was the public announcement that Samsung is in full production with their 32-nm HKMG process, and it appears in Austin as well as Korea.  I was hoping that we might see it in the new iPad, but we’ve now confirmed that the A5x chip is 45-nm. I guess we’ll have to wait for one of the new phones or tablets that will be out soon. Actually, that includes TVs too – Samsung had a TV with gesture recognition on the show floor, powered by a 32-nm HKMG processor, and that’s due out next month as well.

The following day I was at an Intel analyst meeting, but that’s under NDA so I can’t say too much; but it’s not letting too much out to say that it reinforced their messages from CES and the Mobile World Congress that there will be a big push on Ultrabooks and mobile phones.  Next month expect a huge marketing campaign for Ultrabooks – it was described as “epic” and “cinematic” at CES. Even now we’re seeing all sorts of product announcements by the OEMs, including plenty with the 22-nm Ivy Bridge chip inside.

At the moment I’m in Shanghai taking in the China Semiconductor Technology International Conference and Semicon China. I’m presenting on “Recent Innovations in Leading-Edge Silicon Devices”; hopefully it will get a good reception. And we’ll see if there’s anything blog-worthy this week. In the meantime I tweet @ChipworksDick if anything is noteworthy.